熱間鍛造プレス Massey 2800 - 2800 トン
Massey 2800 熱間鍛造プレス - 説明
技術仕様 Massey 2800 (ID:S91152)
| Type | Hot forging press |
|---|---|
| Manufacturer | Massey |
| Model | 2800 |
| Capacity | 2800 ton |
| Stroke Length | 355 mm |
| SPM | 60 |
| Max Working Strokes/Min | 20 |
| Shut Height with Ram at TDC | 1245 mm |
| Shut Height with Ram at BDC | 890 mm |
| Shut Height Stroke Adjustment | +5 mm & -14 mm |
| Ram Dimensions | 1219 x 1118 mm |
| Bed Size | 1219 x 1040 mm |
| Width Between Columns | 1422 mm |
| Width of Opening in Columns | 864 mm |
| Ram Ejector Stroke | 35 mm |
| Table Ejector Stroke | 0-60 mm |
| Journal Diameter | 584 mm |
| Shaft Diameter at Eccentric | 940 mm |
| Wedge to Floor | 585 mm |
| Wedge Dimensions (Front to Back) | 1040 mm |
| Floor Space | 3650 mm x 4950 mm |
| Height Above Floor | 5943 mm |
| Motor Size (Continuous Rating) | 150 KW |
| Motor Speed at Full Load | 985 rpm |
| Weight (Gross) Including Girders and Preload | 170 tons |
熱間鍛造プレス Massey - 技術プロセスと操作
| 鍛造 | 金属の塑性変形プロセスであり、素材は打撃または静的圧力の作用を受けて形状を変化させます。鍛造中に金属組織は緻密化し、内部の不均一性が除去され、材料の機械的特性が向上します。これにより、鍛造製品は大きな荷重下での高い強度と信頼性が特徴となります。鍛造は、完成部品の製造と、後続のスタンピングのための素材準備の両方に使用されます。 |
|---|---|
| 熱間鍛造 | 熱間鍛造は、高温下で金属を圧力成形するプロセスです。加熱により材料の変形抵抗が低下し、金型キャビティへの流動が容易になります。高い生産性と複雑な形状の成形が可能です。鋼および合金からの鍛造品の量産・大量生産に使用されます。 |
| 閉塞金型鍛造 | 素材は金属の流動を制限する金型キャビティ内で変形し、工具の正確な形状を満たすように強制されます。高圧の下で材料は金型のあらゆる凹部と細部に広がり、正確な形状を持つ部品を生み出します。この方法は高い精度と再現性を提供し、複雑な鍛造品の量産および大量生産の標準となっています。 |
| 予備成形 | 予備成形は、素材を本スタンピング作業に向けて準備し、将来の部品のおおよその形状を与えます。金属は金型内で分配され、最終的な充填を容易にし、工具の摩耗を低減します。この中間段階により、完成品の精度と品質が向上します。 |
| ピアシング | ピアシングは、材料を除去せずに工具を素材に押し通すことで、塊状素材に穴を形成します。金属は側方に押しのけられ、周囲の組織を保ちながら貫通穴または止まり穴が作られます。この作業はプレスで行われ、ブッシュ、リング、シャフトなどの中空部品の製造に使用されます。 |