熱間鍛造プレス TMP Voronezh KG8040 - 1000 トン
TMP Voronezh KG8040 熱間鍛造プレス - 説明
技術仕様 TMP Voronezh KG8040 (ID:76085)
| Type | Hot forging press |
|---|---|
| Manufacturer | TMP Voronezh |
| Model | KG8040 |
| Year of manufacture | 1985 |
| Year of overhaul | 2022 |
| Force | 1000 ton |
| Slide stroke | 380 mm |
| Frequency of continuous slide strokes | 40/1 min |
| Distance between table and punch plate of slider in case of upper table location | 710 mm |
| Adjustment of distance between table and slider | 10 mm |
| Distance between columns | 1000 mm |
| Table dimensions | |
| Left-to-right | 930 mm |
| Front-to-back | 1000 mm |
| Slider dimensions | |
| Left-to-right | 780 mm |
| Front-to-back | 1000 mm |
| Bottom ejector | |
| Stroke | 280 mm |
| Power | 10 kN |
| Feed step | 200 mm |
| Main drive power | 110 kW |
| Overall dimensions | |
| Width | 4880 mm |
| Length | 3920 mm |
| Height above floor | 5860 mm |
| Total weight | 90000 kg |
熱間鍛造プレス TMP Voronezh - 技術プロセスと操作
| 鍛造 | 金属の塑性変形プロセスであり、素材は打撃または静的圧力の作用を受けて形状を変化させます。鍛造中に金属組織は緻密化し、内部の不均一性が除去され、材料の機械的特性が向上します。これにより、鍛造製品は大きな荷重下での高い強度と信頼性が特徴となります。鍛造は、完成部品の製造と、後続のスタンピングのための素材準備の両方に使用されます。 |
|---|---|
| 熱間鍛造 | 熱間鍛造は、高温下で金属を圧力成形するプロセスです。加熱により材料の変形抵抗が低下し、金型キャビティへの流動が容易になります。高い生産性と複雑な形状の成形が可能です。鋼および合金からの鍛造品の量産・大量生産に使用されます。 |
| 閉塞金型鍛造 | 素材は金属の流動を制限する金型キャビティ内で変形し、工具の正確な形状を満たすように強制されます。高圧の下で材料は金型のあらゆる凹部と細部に広がり、正確な形状を持つ部品を生み出します。この方法は高い精度と再現性を提供し、複雑な鍛造品の量産および大量生産の標準となっています。 |
| 予備成形 | 予備成形は、素材を本スタンピング作業に向けて準備し、将来の部品のおおよその形状を与えます。金属は金型内で分配され、最終的な充填を容易にし、工具の摩耗を低減します。この中間段階により、完成品の精度と品質が向上します。 |
| ピアシング | ピアシングは、材料を除去せずに工具を素材に押し通すことで、塊状素材に穴を形成します。金属は側方に押しのけられ、周囲の組織を保ちながら貫通穴または止まり穴が作られます。この作業はプレスで行われ、ブッシュ、リング、シャフトなどの中空部品の製造に使用されます。 |